Grade:LE913C
Product: Hot Melt Adhesive Granules For Various Multi-Layer Plastic Medicine Bottles
Advantages
Strong Adhesion:Adhere to EVOH etc. strongly by thermal reaction. And it bonds strongly to PE resins with EVOH and keeps its polyolefin characteristics as well.
Durability:It can maintain excellent adhesiveness under the the harsh conditions in the thermal aging , hot water, cold water, low temperature,etc.
Simple and easy processing: It can be processed in conventional extrusion equipment which is designed for plyolefin processing,doesn’t require special production equipment and the process condition is similar to common polyolefin.
Decriptions
LE913C is a maleic anhydride functionalized polyethylene mixture, easy to form film, with excellent processability and adhesive strength.
Chemical Structure
Composition: Maleic Anhydride fuctionalized polyethylene mixture.
Application
LE913C is widely used as a binder for all kinds of multi-layer plastic medicine bottles.
Physical Properties
| |
Test Method |
Unit |
LE913C |
| Appearance |
Visual method |
|
Pellets |
| Density |
ASTM D1505 |
g/cm3 |
0.93 |
| MFI |
ASTM D-1238
190℃/2.16kg
|
g/10min |
2.2 |
| Shore Hardness |
ASTM D2240 |
|
66 |
| Elongation at Break |
ASTM D638 |
% |
＞800 |
| Tensile Breaking Strength |
ASTM D638 |
MPa |
23.3 |
| Tensile Yield Strength |
ASTM D638 |
MPa |
11.4 |
| Melting Point |
ASTM D3418 |
10℃/min |
127 |
| Vicat Softening Point |
ASTM D-1525 |
2℃/min |
86 |
Remark: These are typical properties only and are not to be regarded as sales specifications
Adhesive Strength Test Process
| Machine Type |
Working Temp(℃) |
Test Speed(mm/min) |
Pressure(kgf/cm2) |
| Heat Roll-presser |
130-150 |
3,000 |
2.5~3.5 |
Packages and Storage
- Packed in 25kgs Paper-plastic bags
- Keep in dry,cool and ventilated environment;Avoid direct exposure to water and sunlight.Avoid bulk package and securely wrap the unused part.
- Guarantee period: 12 Months.
Product Tags:
|
|
PE Hot Melt Adhesive Granule Long Lasting Stable Adhesion For Plastic Medicine Bottles Images
|